Microcrystalline ceramic materials
ZAS1550 microcrystalline ceramic material is a high-temperature ceramic material composed of high-strength silicon carbide composite and microcrystalline bonding. The compressive strength and flexural strength at high temperatures are very high, and it has excellent resistance to high temperature rapid cooling and heating, especially suitable for applications such as acid alkali corrosion at high temperatures. Microcrystalline ceramic materials have good impact resistance at high temperatures and are suitable for applications with high temperature impact, high material wear, and high material corrosion. The product is equipped with specialized installation anchor material to achieve better service life.
Key words:
Microcrystalline ceramic materials
Classification:
Products
Product accessories:
Hotline:
Microcrystalline ceramic materials
Graphic Details
ZAS1550 microcrystalline ceramic material is a kind of high-temperature ceramic material composed of high-strength silicon carbide composite microcrystalline combination, compressive strength and flexural strength at high temperature is very high, with excellent high temperature resistance to quenching and hot resistance, especially suitable for acid and alkali corrosion and other applications at high temperature. Microcrystalline ceramic materials have good impact resistance at high temperature, which is suitable for applications with high temperature impact, large material wear and high material corrosion. The products are equipped with special installation anchor materials to achieve better service life.
Product use
•High temperature impact resistance•High temperature wear resistance•High temperature thermal shock resistance•High temperature corrosion resistance
Specifications
Plate • 200 × 200 × 35 mm • 200 × 100 × 35 mm
Thickness|
35, 40mm, other thicknesses can also be customized
Safe
microcrystalline ceramic material is a polycrystalline inorganic non-metallic material, the raw materials are environmentally friendly and harmless raw materials, without any toxic effect on the human body, and is also an environmentally friendly ceramic material.
Product performance
|
color |
grey |
|
Maximum operating temperature |
1550℃ |
|
Long-term use temperature |
1450℃ |
|
density |
2.8g/cm3 |
|
compressive strength |
≥150 MPa |
|
Flexural strength |
≥20MPa |
|
Abrasion |
0.03g/cm2 |
|
Thermal shock resistant 1100°C water cooling |
≥ 20 times |
|
Chemical Composition % |
|
|
SiC SiO2 + Si3N4 + other |
80% 20% |
|
Thermal conductivity 1000℃ |
W/ mK 15 |
Previous Page
Microcrystalline ceramic materials
Next Page
Previous Page
Next Page
Related Products
Consulting
Has long been engaged in the promotion and application of refractory insulation materials, and has rich experience in the application of industrial kiln thermal design and insulation materials....
Shanghai Address: Floor 5, Building 13, No.68 Zhongchuang Road, Songjiang District, Shanghai
Tianjin Address: Tianjin Binhai High-tech Zone Haitai Development Road No. 6 K1-2-602
Operator:022-83726551/552/553 83726554(straight)
Mailbox:info@nanjistar.cn
Website:www.nanjistar.cn
Service Hotline:400-022-0408
Copyright©2023 shanghai antarctic high-tech co., ltd